NYHP-7300H
低介電常數(shù)(Dk 2.98@10GHz)
介質(zhì)損耗(Df 0.0015@10GHz)
Tg >180℃ 高耐熱性
優(yōu)異通孔可靠性及PCB加工性
默認(rèn)使用HVLP銅
-
高性能天線/基站High performance Antenna/Base Station
NYHP-7300H 基板產(chǎn)品規(guī)格表 Specification Sheet for Laminate
| NYHP-7300H 覆銅板 NYHP-7300H Laminate | 測試方法 Test Method | 條件 Condition | 單位Units | 典型值 Typical Value |
| IPC-TM-650 | Metric(English) | 1.524mm CCL | ||
| 剝離強(qiáng)度 Peel Strength | 2.4.8 | 1oz HVLP | N/mm(lb/inch) | ＞0.7 (4.0) |
| 體積電阻 Volume Resistivity 恒溫恒濕C-96/35/90 | 2.5.17.1 | COND A | MΩ-cm Minimu | 4×108 |
| 表面電阻 Surface Resistivity 恒溫恒濕C-96/35/90 | 2.5.17.1 | COND A | MΩ Minimum | 2.1×108 |
| 吸水率 Water Absorption | 2.6.2.1 | — | % Maximum | 0.14 |
| 介電常數(shù)Dk Permittivity | 諧振環(huán) | 2 GHz/23℃ | Maximum | 2.98 ± 0.05 |
| 2.5.5.5C | 10 GHz/23℃ | Maximum | 2.98 ± 0.05 | |
| 介質(zhì)損耗Df Loss Tangent | 2.5.5.5C | 10 GHz/23℃ | Maximum | 0.0015 |
| SPDR | 10 GHz/23℃ | Maximum | 0.0014 | |
| TCDK | 2.5.5.5 | -50℃-150℃ | PPM/℃ | 40 |
| 彎曲強(qiáng)度 Flexural Strength A. 縱向 Length Direction B. 橫向 Cross Direction | ASTM D790 | RT | N/mm2 Minimum | 210 155 |
| 熱應(yīng)力沖擊 Thermal Stress A. 未蝕刻 Unetched B. 蝕刻 Etched | 2.4.13.1 | 288℃ | 10 sec at 288℃ | Pass Pass |
| 耐燃性 Flame Resistance ( Laminate & Prepreg as laminated) | UL94 （UL File: E213990) | — | Rating | V-0 |
| 玻璃態(tài)轉(zhuǎn)換溫度Tg Glass Transition Temperature | 2.4.24 | DMA | ℃ | >180 |
| 熱分解溫度Td Decomposition Temperature | TD (5% wt loss) | — | ℃ | >380 |
| Z 軸膨脹系數(shù) Z-axis CTE (50-260℃) a1 ( 50 to 100 ℃) a2 ( 200 to 260 ℃) | 2.4.24 | — | % PPM/℃ PPM/℃ | 3.2 50 280 |
| 耐熱性(除去銅箔) Thermal Resistance (Copper Removed) A.T260 B.T288 C.T300 | 2.4.24.1 | — | Minutes Minutes Minutes | >120 > 60 > 60 |
| 耐CAF性能 CAF Resistance | 2.6.25 | AABUS | Pass/Fail | Pass |
| PIM | 800/1800/2600 MHz | — | dBc | ≤-158 |